Some mechanical properties of lanthanum metal
AuthorSchuyler, Donald Richard
AdvisorWinston, J. S.
Geological Sciences and Engineering
AltmetricsView Usage Statistics
Recovery, recrystallization, hardness, and x-ray studies were made on a commercially produced lanthanum metal„ Arc melted lanthanum was cold worked and vacuum annealed to provide specimens for testing. Lanthanum of this purity was found to work harden rapidly and therefore fail with relatively low amounts of cold work. Definite recrystallization phenomena were not determined although recrystallization is postulated to start in the 40QOC region, with recovery starting at approximately 175° to 250°C.
Online access for this thesis was created in part with support from the Institute of Museum and Library Services (IMLS) administered by the Nevada State Library, Archives and Public Records through the Library Services and Technology Act (LSTA). To obtain a high quality image or document please contact the DeLaMare Library at https://unr.libanswers.com/ or call: 775-784-6945.