Evidence of and analysis of vacancy diffusion during anodic dissolution of thin film Cu/Ag couples
AuthorDavidson, Gail A.
AdvisorJones, Denny A.
Mining and Metallurgical Engineering
AltmetricsView Usage Statistics
Vacancy diffusion during anodic dissolution of thin film Cu/Ag couples was studied and documented.
Online access for this thesis was created in part with support from the Institute of Museum and Library Services (IMLS) administered by the Nevada State Library, Archives and Public Records through the Library Services and Technology Act (LSTA). To obtain a high quality image or document please contact the DeLaMare Library at https://unr.libanswers.com/ or call: 775-784-6945.